High-Temperature Oxidation Protective Coatings for Vanadium-Base Alloys

Author(s): J. J. Rausch and F. C. Holtz
Corporate Author: Armour Research Foundation
Corporate Report Number: ARF-B6000-2
Date of Publication: 1963-02-09
Pages: 10
Contract: N600(19)59182
AD Number: AD0296760
Original AD Number: AD-296 760

Abstract:
Processing variables relating to the pack-siliconizing of V-5w/o Ti-20w/o CB and V-1w/o Ti-60w/o Cb are being studied. Samples coatedd at 2010, 2190. and 2370 F show that coating growth rate is time dependent up to 16 hours. Silicide coatings have been applied to eleven vanadium alloys currently under development, and no failures have been observed after 15 to 35 hours in 2200 F air. Tensile and other specimens of V-1w/o Ti-60w/o Cb have been pack-siliconized for evaluation by aerospace and other organizations. Compounds of V-Cb-Ni were flame-sprayed on V-1w/o Ti 60w/o Cb, but excessive porosity caused rapid failure in 2000 and 2200 F air. Diffusion couples of nickel and the V-Cb-Ti alloy were reacted at 2000 and 22000 F for 24 and 8 hours, respectively, with very slight hardening of the vanadium alloy.

This citation is provided as a resource for researchers, but Contrails cannot provide a full-image download

U.S. government employees, Military/Department of Defense employees, and U.S. government contractors and sub-contractors may be eligible to register with the Defense Technical Information Center (DTIC), where this report and others like it may be available

Other options for obtaining this report

Via the Defense Technical Information Center (DTIC):
This report is not publicly available via DTIC

Via National Technical Information Service:
This report is unlikely to be available in the National Technical Reports Library

Indications of Public Availability
No digitial image of an index entry indicating public availability is currently available
There has been no verification of an indication of public availability from an inside cover statement
Tags: