Physical Properties Of High Temperature Materials. Part Vi. Enthalpy And Heat Capacity Of Magnesium Oxide, Zirconium Oxide, And Zirconium Silicate From 0 To 900 C
Report Number: WADC TR 57-374 Part 6
Author: Victor, Andrew C.
Author: Douglas, Thomas B.
Corporate Author: National Bureau Of Standards Washington D C
Laboratory: Materials Central
Date of Publication: 1960-12
Pages: 22
Contract: AF 33(616)-5621
Project: 7360
Task: 73603
AD Number: AD0258383
Abstract: The heat contents of three refractory substances, magnesium oxide, zirconium oxide, and zirconium silicate were measured relative to 0 C at 100degree intervals up to 900 C, using a precise drop calorimetric method. The magnesium oxide sample was of high purity. The other samples, however, were of relatively low purity. No attempt was made to correct heat-content and heat-capacity values for impurities. Specific heats were derived from and described by equations in calories per gram-deg C. The specific heats from these equations were compared with values from the literature.
Provenance: Lockheed Martin Missiles & Fire Control
Other options for obtaining this report
Via the Defense Technical Information Center (DTIC): A record for this report, and possibly a full-image download of the report, exists at DTIC Via National Technical Information Service: This report may have been digitized and made freely available for public download, or made publicly available for purchase by the National Technical Information Service through their online database, the National Technical Reports Library Indications of Public Availability No digital image of an index entry indicating public availability is currently available The inside cover of this report indicates that it was released for public saleRelated Reports
This report has the following parts/volumes:
-
Physical Properties Of High Temperature Materials. Part I: New apparatus for The Precise Measurement Of Heat Content And Heat Capacity From 0o to 1500oC
WADC TR 57-374 Part 1 -
Physical Properties Of High Temperature Materials. Part II: TheHeat Capacity Of Zirconium, Several Zirconium Hydrides, And Certain Cladding Materials From 0o to 900oC; Relation To Other Thermodynamic Properties Of The Zr-H System
WADC TR 57-374 Part 2 -
Physical Properties Of High Temperature Materials. Part III: The Thermal And Electrical Conductivities Of Several Zirconium Hydrides Up To 800 Degrees C
WADC TR 57-374 Part 3 -
Physical Properties Of High Temperature Materials. Part IV: Thermal Diffusivity Apparatus For 100 Degrees To 1,500 Degrees C
WADC TR 57-374 Part 4 -
Physical Properties Of High Temperature Materials. Part V: Thermal Diffusivity OF Magnesia-Stabilized Zirconium Oxide At high Temperatures
WADC TR 57-374 Part 5