Procedure For Evaluation Of Coated Refractory Alloys

Report Number: ML TDR 64-70
Author: Levinstein, M. A.
Author: Marble, J. D.
Corporate Author: General Electric Co Cincinnati Ohio
Laboratory: AF Materials Laboratory
Date of Publication: 1964-06
Pages: 204
Contract: AF 33(616)-8154
Project: None Given
AD Number: AD0604738

Abstract:
Procedures for the evaluation of coated molybdenum and columbium alloys were investigated. A simple corrugated specimen was designed to determine the applicability of current coatings to a fabricated structure. Coated specimens were oxidation tested at 2500F up to 10 hours, and sectioned for metallographic examination and hardness determination. Dynamic oxidation tests were conducted using a gas-fired flame tunnel and a plasma test stand. Effects of the coatings and elevated temperature exposure on basis metal properties were established by combined stress, fatigue, and tensile tests. Coatings from six sources were investigated on the program. Based on the results obtained recommendations are made for the standardization of the applicability specimen and combined stress testing along with other mechanical tests for the evaluation of coated refractory metals.


Provenance:
Lockheed Martin Missiles & Fire Control
Download this report

(PDF, 7.29 MB, 204 pages)

Other options for obtaining this report

Via the Defense Technical Information Center (DTIC):
A record for this report, and possibly a full-image download of the report, exists at DTIC

Via National Technical Information Service:
This report may have been digitized and made freely available for public download, or made publicly available for purchase by the National Technical Information Service through their online database, the National Technical Reports Library

Indications of Public Availability
No digital image of an index entry indicating public availability is currently available
The inside cover of this report indicates that it was released for public sale