Dynamic Behavior of Metals Under Tensile Impact. Part II: Annealed and Cold Worked Materials.

Report Number: AFML TR 69-76 Part II
Author: Schultz, Albert B.
Corporate Author: University of Illinois at Chicago Circle, Department Of Materials Engineering
Laboratory: Air Force Materials Laboratory
Date of Publication: 1969-06
Pages: 46
Contract: F33615-67-C-1283
Project: 7351 - Metallic Materials
Task: 735106 - Behavior of Metals
AD Number: AD0857984

Abstract:
The mechanical behavior of metals subjected to uniaxial tensile impact at room temperature is reported. Tests were conducted on 1100 aluminum subjected to light and to heavy, cold working; 2024 aluminum after annealing and after light and heavy cold working; C1010 steel in these same three conditions; and OFHC copper and 70-30 brass in an annealed state. In five of the ten series the materials were found to possess dynamic stress-strain curves which fell below the static curves. The yield point of the steel was lowered by impact loading. Ratios of dynamic to static ultimate stress were found to range from 0.59 to 1.3.


Provenance:
Lockheed Martin Missiles & Fire Control
Download this report

(PDF, 1.09 MB, 46 pages)

Other options for obtaining this report

Via the Defense Technical Information Center (DTIC):
A record for this report, and possibly a full-image download of the report, exists at DTIC

Via National Technical Information Service:
This report may have been digitized and made freely available for public download, or made publicly available for purchase by the National Technical Information Service through their online database, the National Technical Reports Library

Indications of Public Availability
No digital image of an index entry indicating public availability is currently available
There has been no verification of an indication of public availability from an inside cover statement
Tags:

Related Reports

This report has the following parts/volumes: